Studies on functional improvement by deforming colloidal particles

2023 Fiscal Year Final Research Report

• Project/Area Number: 21K05164
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 35010:Polymer chemistry-related
• Research Institution: Chiba University
• Principal Investigator: TANIGUCHI Tatsuo 千葉大学, 大学院工学研究院, 教授 (30292444)
• Project Period (FY): 2021-04-01 – 2024-03-31
• Keywords: 高分子微粒子 / 表面改質 / 内包化 / 液晶 / ヘテロ凝集 / 微小圧縮試験 / 液晶カプセル

Outline of Final Research Achievements

Printed electronics (PE) is attracting attention as a next-generation device fabrication technology, and the development of inks and toners applicable to PE is an important issue. The use of polymer colloidal materials ranging from several tens of nanometers to several micrometers in size complexed with functional materials is considered to be effective in improving functionality in terms of hydrodynamic properties, dispersion/aggregation properties, and anisotropic function transfer. In this study, we attempted surface modification of spherical solid particles and encapsulation of liquid crystalline compounds inside the particles.

Free Research Field

高分子化学

Academic Significance and Societal Importance of the Research Achievements

本研究では，真球状の中実粒子や中空粒子などの高分子コロイド材料を対象として，表面改質および内部への機能材料の内包化による機能化について検討した。ニッケルめっき粒子と高分子微粒子とを媒体中で撹拌するだけの操作により，異方性導電性フィルムなど工業的に応用可能な材料を調製することができた。また，高分子微粒子にシード重合の手法を適用することにより，電場に応答する液晶カプセルを作製することができたことから，プリンテッドエレクトリニクスに応用が期待できる。