2012 Fiscal Year Final Research Report
Gas Recycling Process of Magnesium Alloy Scrap
Project/Area Number |
22560743
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Metal making engineering
|
Research Institution | National Institute of Technology, Toyama College |
Principal Investigator |
INOUE Makoto 富山高等専門学校, 機械システム工学科, 教授 (30232557)
|
Project Period (FY) |
2010 – 2012
|
Keywords | リサイクル / マグネシウム / 真空蒸留法 / 押出加工 |
Research Abstract |
Gas recycling of the magnesium alloy by the vacuum distillation examined in distillation time 2-5h for raw materials temperature 600℃, condense temperature310-350℃, and there was not the clear difference in this condense temperature range. The extrusion load grew big so that I examined the production condition of extrusion temperature 350-400 ℃ of the extrusion, extrusion ratio R8-16 as gas recycling materials provided in vacuum distillation, and extrusion temperature was low or so that the extrusion ratio was big. Raw materials Mg-Al-Zn alloy was harder than raw materials Mg-Al-Mn alloy, and the hardness of magnesium gas recycling extrusions, the strength came to have a big strength. The corrosion resistance was good, and the influence of the extrusion temperature did not have the clear difference.
|