Construction of solderling method for zirconia by Ag-Cu-Sn-Ti solderling material

2023 Fiscal Year Final Research Report

• Project/Area Number: 22K17119
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 57050:Prosthodontics-related
• Research Institution: Nihon University
• Principal Investigator: HONDA Junichi 日本大学, 歯学部, 助教 (50800942)
• Project Period (FY): 2022-04-01 – 2024-03-31
• Keywords: 活性金属ろう材 / ジルコニア / インプラント上部構造

Outline of Final Research Achievements

A solderling method for dental zirconia using Ag-Cu-Sn-Ti solderling material was verified on a specimen according to ISO 9333. Solderling cores were fabricated and soldered in a porcelain furnace. However, the Ag-Cu-Sn-Ti solderling material reacts easily with oxygen and could not be soldered in the porcelain furnace due to the lack of vacuum. In addition, it was observed that theAg-Cu-Sn-Ti solderling material was oxidized by the zirconia because of its oxygen content.
Therefore, a solderling method using a feldspathic porcelain, which has good shear bonding strength with zirconia, was investigated, but the result was less than the 250 MPa standard. This study indicates that solderling of zirconia may be difficult.

Free Research Field

歯科補綴学

Academic Significance and Societal Importance of the Research Achievements

本研究は歯科用ジルコニアのろう付け法の構築を目的としたが、歯科用ジルコニアには、酸素が含まれており、ろう付け中に活性金属ろう材が酸化し、ろう付けが困難であることが確認された。また、ジルコニアと良好なせん断接着力を有しているジルコニア用前装用陶材を用いてのろう付け法を検討したが、基準である250MPaにおよばない結果となった。
本研究から、ジルコニアのろう付けは困難であることが示された。しかし、モノリシック構造で用いることで、機械的強度に優れたブリッジの製作が可能であり、その臨床応用に際しての有用性がさらに向上したことが示唆された。