2014 Fiscal Year Final Research Report

Improvements of properties of Cu-based alloys by aging in hydrogen atmosphere in being associated with new precipitation mode

Research Project

  • PDF
Project/Area Number 23246123
Research Category

Grant-in-Aid for Scientific Research (A)

Allocation TypeSingle-year Grants
Section一般
Research Field Material processing/treatments
Research InstitutionTohoku University

Principal Investigator

OKADA Masuo  東北大学, 工学(系)研究科(研究院), 名誉教授 (80133049)

Co-Investigator(Kenkyū-buntansha) KAMEGAWA Atsunori  東北大学, 大学院工学研究科, 准教授 (90292242)
Research Collaborator KURIIWA Takahiro  
Project Period (FY) 2011-04-01 – 2015-03-31
Keywords水素 / Cu-Ti合金 / Cu-Cr-Zr合金 / Cu-Cr-Zr-Ti合金 / スピノーダル分解 / 水素中時効熱処理 / 水素有効機能
Outline of Final Research Achievements

Effects of hydrogen heat-treatment on mechanical and electrical properties of commercialized copper-based alloy were investigated.
Optimum composition of Cu-Ti alloy for strength enhancement by hydrogen heat-treatment was Cu-3mass%Ti. It was found that hydrogenation followed by heat-treatment in vacuum was effective to enhance the workability of the alloys and its electrical conductivity.
The addition of Ti into Cu-Cr-Zr alloys heat-treated in hydrogen was effective to improve their tensile strength. The tensile strength and electrical conductivity of the Cu-0.2Cr-0.6Zr-0.5Ti alloy after hydrogen heat-treatment at 400C for 5h were 665MPa and 56%IACS, respectively.

Free Research Field

材料工学