2013 Fiscal Year Final Research Report
Synthesis of nano phosphor and application to EL devices
| Project/Area Number |
23350094
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Functional materials/Devices
|
|---|
| Research Institution | National Institute of Advanced Industrial Science and Technology |
|---|
Principal Investigator |
HAKUTA Yukiya 独立行政法人産業技術総合研究所, ナノシステム研究部門, 主任研究員 (30250707)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
SUE Kiwamu 産業技術総合研究所, ナノシステム研究部門, 主任研究員 (60333845)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
TAKASHIMA Hiroshi 産業技術総合研究所, 光電子研究部門, 主任研究員 (10357353)
|
|---|
| Project Period (FY) |
2011-04-01 – 2014-03-31
|
| Keywords | 電気・磁気デバイス / ナノ蛍光体 / 水熱合成 / ＥＬデバイス |
|---|
| Research Abstract |
We have successfully synthesized rare earth metal ion doped Perovskite type metal oxide nanophosphor via hydrothermal reaction under supercritical water conditions. The size of the particles obtained was in the range from 20 to 40 nm. The quantum efficiency of the nanophosphors was 12 % being comparable to that of bulk materials. The prototype dispersion electroluminescence (EL) element used the nanophosphors obtained showed the typical electroluminescence behaviors under an electric field of 350 V at 1 kHz. Furthermore, EL was observed under an electric field of low voltages by depressing the thickness of the dispersion layer to around 10 micron meter. These results show that metal oxide nanophosphors can be applicable to a novel dispersion electroluminescence device.
|
-
-
-
[Journal Article] Ultrafast Hydrothermal Synthesis of Pr-doped Ca0. 6Sr0. 4TiO3 Red Phosphor Nanoparticles using Corrosion Resistant Microfluidic Devices with Ti-lined Structure under High-Temperature and High-Pressure Condition2013