2013 Fiscal Year Final Research Report
Construction of the crack-less maicro-cutting technology of the biodegradable polylactic acid material used for a medical-application fixture
| Project/Area Number |
23560140
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Production engineering/Processing studies
|
|---|
| Research Institution | Kanazawa Institute of Technology |
|---|
Principal Investigator |
KATO HIDEHARU 金沢工業大学, 工学部, 教授 (90278101)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
SHINTANI Kazuhiro 金沢工業大学, 工学部, 教授 (80139758)
MORIMOTO Yoshitaka 金沢工業大学, 工学部, 教授 (00290734)
OHSAWA Satoshi 金沢工業大学, 工学部, 教授 (50259636)
|
|---|
| Project Period (FY) |
2011 – 2013
|
| Keywords | ポリ乳酸 / 微細加工 / クラックレス / ダイヤモンド工具 |
|---|
| Research Abstract |
In brain surgery, application to the fixture of polylactic acid material is expected, Because, it is for polylactic acid producing neither excelling in biocompatibility, nor an artifact. This research is aimed at construction of the micro fabrication method which controls the micro-crack generated on the machined surface.
As a result of detailed observation about the micro-cutting behavior in a fundamental orthogonal cutting using a high-speed video camera, shear angle during cutting of this material showed the same tendency as a plastic material, and shows a very large angle. Moreover, the viscoelastic property and the cutting temperature of material were measured and it showed clearly to create the machined surface of crack-less in case of the cutting-temperature conditions similar to glass transition temperature.
|