2013 Fiscal Year Final Research Report
Investigation of mechanism for enhancement on recombination of point deffects at controlled precipitate/matrix interface
| Project/Area Number |
23760804
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Multi-year Fund |
|---|
| Research Field |
Nuclear fusion studies
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2011 – 2012
|
| Keywords | 析出物 / 照射損傷 / 界面 / シンク / 銅合金 / ステンレス鋼 / ボイド |
|---|
| Research Abstract |
It is known that precipitate/matrix interface act as sinks for point defects. However, it have not been clarified the relation between structure and sink efficiency of interfaces. In this study, we observed the several types of interface such as Cr-precipitate in Cu-Cr system, carbide and siliside in austenitic stainless steel by three dimensional atom probe. The results of formation behavior of point defects under irradiation shows that semicoherent precipitate/matrix interface, which have specific orientation relationships act as neutral sinks.
|