Development of Innovative Ultrahigh-Speed Grinding Systems Using Ultrafine-Crystalline cBN Abrasive Grains
| Project/Area Number |
19560106
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Production engineering/Processing studies
|
|---|
| Research Institution | Utsunomiya University |
|---|
Principal Investigator |
ICHIDA Yoshio Utsunomiya University, 大学院・工学研究科, 教授 (50091939)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
SATO Ryunosuke 宇都宮大学, 大学院・工学研究科, 助教 (20312861)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000)
Fiscal Year 2008: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
Fiscal Year 2007: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
|
|---|
| Keywords | 切削・研削加工 / 超高速研削システム / 超微結晶cBN砥粒 / 磁気軸受けスピンドル / cBN ホイール / 砥粒切れ刃摩耗 / 研削エネルギー / 機械工学・生産工学 / cBNホイール / 研削能率 / 機械工作・生産加工 / 磁気軸受スピンドル |
|---|
| Research Abstract |
本研究は, ナノメータオーダの超微細一次cBN粒子が緻密に結合した結晶構造を有する新しいタイプの超微結晶cBN砥粒(UcBN)を開発すると共に, それを用いた次世代高性能UcBNホイールを試作し, その研削性能を評価したものである. この結果, UcBN砥粒は従来のcBN砥粒の2~4倍の破壊強度をもち, 優れた耐摩耗性と研削性能を発揮することを明らかにした。さらに, UcBNを用いた超高速研削システムの構築を試み, 200m/s以上の超高速度条件においてもUcBN砥粒が優れた摩耗性および研削性能を示すことを明らかにした.
|