Mn-Ga based Hard Magnets with High Coercivity and Ductility
| Project/Area Number |
22656149
|
|---|
| Research Category |
Grant-in-Aid for Challenging Exploratory Research
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Structural/Functional materials
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
KAINUMA Ryosuke 東北大学, 大学院・工学研究科, 教授 (20202004)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
UMETSU Rie 東北大学, 金属材料研究所, 助教 (60422086)
|
|---|
| Project Period (FY) |
2010 – 2011
|
| Project Status |
Completed (Fiscal Year 2011)
|
| Budget Amount *help |
¥3,550,000 (Direct Cost: ¥3,100,000、Indirect Cost: ¥450,000)
Fiscal Year 2011: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2010: ¥1,600,000 (Direct Cost: ¥1,600,000)
|
|---|
| Keywords | ハード磁石 / Mn合金 / 析出 / 磁場中時効 / 結晶磁気異方性 / ハード磁石材料 / 希土類フリー / 状態図 / 規則-不規則変態 / 磁気変態 |
|---|
| Research Abstract |
In this project, a rare-earth metal-free magnet is aimed to be developed in the Mn-Ga based alloy systems. Mn-Ga binary and Mn-Ga-X (X : Ni, Co, Cu)ternary phase diagrams have experimentally been determined in the beginning. It was found that the hcp phase suppressing appearance of the ferromagnetic D0_<22> phase exists at high temperatures in the wide composition range and that the situation is not improved by addition of the elements X. On the other hand, a Mn-Ga-Cu alloy showing a large coercivity of about 10kOe has been found.
|