Molecular Character and the Aggregation Structure of Bio-based Polymers in Bulk and Thin Film State
Project/Area Number |
25810077
|
Research Category |
Grant-in-Aid for Young Scientists (B)
|
Allocation Type | Multi-year Fund |
Research Field |
Polymer chemistry
|
Research Institution | Kyushu University |
Principal Investigator |
HIGAKI Yuji 九州大学, 先導物質化学研究所, 助教 (40619649)
|
Project Period (FY) |
2013-04-01 – 2015-03-31
|
Project Status |
Completed (Fiscal Year 2014)
|
Budget Amount *help |
¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
Fiscal Year 2014: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
Fiscal Year 2013: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
|
Keywords | 植物由来樹脂 / ポリマーブラシ / 分子鎖形態 / 高分子薄膜 / トライボロジー / 小角X線散乱測定 / 中性子反射率測定 |
Outline of Final Research Achievements |
We tried to make sure the origin of resin character of a novel non-ester type bio-based polymer, poly(a-methylene-g-butyrolactone) (PMBL) through chain dimension analysis in the solution state and physical characters in the thin film state. The characteristic physical properties is originated from the low free volume and high inter-chain interaction, whereas the chain stiffness is not dominant for the resin character. We also investigated the thin film mechanical properties through microscopic compression test by the use of scanning probe microscopy and macroscopic friction test. We could demonstrate the excellent mechanical properties of the PMBL brush-type thin films.
|