Application of anion removal agent derived from iron and steel slag to waste water treatment and contaminated soil treatment

2019 Fiscal Year Final Research Report

• Project/Area Number: 17K00630
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Research Field: Environmental conscious materials and recycle
• Research Institution: Kansai University
• Principal Investigator: Murayama Norihiro 関西大学, 環境都市工学部, 教授 (90340653)
• Co-Investigator(Kenkyū-buntansha): 林 順一 関西大学, 環境都市工学部, 教授 (60247898) ; 松岡 光昭 関西大学, 環境都市工学部, 助教 (00778160)
• Project Period (FY): 2017-04-01 – 2020-03-31
• Keywords: 鉄鋼スラグ / 有効利用 / 有害陰イオン / 排水処理 / 汚染土壌処理 / 陰イオン除去材

Outline of Final Research Achievements

For the purpose of an effective use of steelmaking slag, the synthesis of various Layard Double Hydroxides (LDHs) with an anion removal ability was conducted by using various steelmaking slags as a starting material. The removal of As(III), B(III), Cr(VI) and Se(IV) in dilute aqueous solution was carried out with the slag-derived LDHs. It is clarified that the obtained slag-LDHs show an excellent removal ability for toxic anionic species in aqueous solution mentioned above. In this study, the possibility is found to apply the slag-LDHs for the environmental purification agent, for example, the treatment of waste water or contaminated soil.

Free Research Field

資源循環工学

Academic Significance and Societal Importance of the Research Achievements

鉄鋼製造過程で大量に副生する鉄鋼スラグ（高炉スラグや製鋼スラグ）に対して、安定した需要が見込める新しい再資源化技術の開発が望まれている。本研究では、いくつかの鉄鋼スラグから陰イオン交換体である層状複水酸化物（LDH）を合成する方法、ならびにそれらを環境浄化の分野で利用する方法について検討を行った。得られた一連の研究結果から、ヒ素やホウ素、クロム、セレンといった水溶液中で陰イオン種を形成する有害物質の除去材としての利用。土壌中に含まれる上述の有害陰イオンの固定化に適用できる可能性が示された。