2022 Fiscal Year Final Research Report
Development of corrosion controlling method by stabilization of rust layer
| Project/Area Number |
19H02215
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Review Section |
Basic Section 22010:Civil engineering material, execution and construction management-related
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
左藤 眞市 地方独立行政法人大阪産業技術研究所, 和泉センター, 総括研究員 (20359409)
土井 康太郎 国立研究開発法人物質・材料研究機構, 構造材料研究拠点, 独立研究者 (80772889)
|
|---|
| Project Period (FY) |
2019-04-01 – 2022-03-31
|
| Keywords | 鉄筋腐食 / 保護性さび / 腐食環境 / ラマン分光分析 |
|---|
| Outline of Final Research Achievements |
The purpose of this research project is to clarify the formation mechanism of the protective rust formed in the process of corrosion in wet and dry cycle environment, and to develop a corrosion controlling method by modifying the rust layer of reinforcing steel in real life concrete structures. It has made clear that non-protective flake type rust forms in a dry and wet cycle environment, but in a relatively stable humidity environment, protective rust can be formed because of slow crystal growth in oxygen-lacking condition. Furthermore, it was confirmed that Fe3O4 with about 50cm-1 Raman shift formed in a humidity-controlled environment. This experimental result shows that and oxygen lacking condition is important for rust layer modification.
|
| Free Research Field |
土木材料、施工および建設マネジメント関連
|
| Academic Significance and Societal Importance of the Research Achievements |
乾湿繰返しによる腐食の進行過程で形成した保護性さびは，緻密で結晶性の高いFe3O4であり，高い耐食性を有しているということが分かってきているが，その生成メカニズムについてはまだ不明な点も多い．保護性さびの生成メカニズムや生成条件を明らかにすることは学術的な意義があると考えている．また，鉄筋腐食はコンクリート構造物の抱える深刻な劣化のひとつであるため，腐食環境の制御により，現場で腐食進行過程にある鉄筋に生じたさび層を改質し，腐食抑制効果を高めることができれば，構造物の老朽化対策に要する費用を大きく低減できると期待され，社会的な意義は大きいと考えられる．
|